PDF#36-1451: QM=Star(+); d=Diffractometer; I=Diffractometer
Zincite, syn
Zn O (Colorless)
Radiation=CuKa1 Lambda=1.5405981 Filter=Graph
Calibration= d-Cutoff=17.7 I/Ic(RIR)=
Ref= McMurdie, H., Morris, M., Evans, E., Paretzkin, B., Wong-Ng, W., Ettlinger, L., Hubbard, C.
Powder Diffraction, 1 76 (1986)
Hexagonal - Powder Diffraction,  P63mc (186) Z=2 mp=
Cell=3.2498x5.2066 Pearson=hP4 (S Zn)
Density(c)=5.675 Density(m)=6.43A Mwt=81.38 Vol=47.62 F(27)=129.6(.0072,29)
Ref= 1. Bragg, W.
Philos. Mag., 39 647 (1920)
Strong Line: 2.48/X 2.81/6 2.60/4 1.62/3 1.48/3 1.91/2 1.38/2 1.36/1 0.91/1 1.09/1
NOTE:  The sample was obtained from the New Jersey Zinc Co., Bethlehem, Pennsylvania, USA.
References to other early patterns may be found in reference (5).
The structure was determined by Bragg (1) and refined by Abrahams, Bernstein (2).
A high pressure cubic NaCl-type of ZnO is reported by Bates et al.
(3) and a cubic, sphalerite type is reported by Radczewski, Schicht (4).
The approximate temperature of data collection was 26 C.
To replace 00-005-0664 (5).
See ICSD 31052 (PDF 01-075-1526).
d(A)     I(f)   I(v)  h  k  l  n^2  2-Theta   Theta  1/(2d)   2pi/d  
 2.814   57.0   50.0  1  0  0        31.769  15.885  0.1777  2.2326
 2.603   44.0   42.0  0  0  2        34.421  17.211  0.1921  2.4135
 2.475  100.0  100.0  1  0  1        36.252  18.126  0.2019  2.5377
 1.911   23.0   30.0  1  0  2        47.538  23.769  0.2616  3.2877
 1.624   32.0   49.0  1  1  0        56.602  28.301  0.3077  3.8672
 1.477   29.0   49.0  1  0  3        62.862  31.431  0.3385  4.2537
 1.407    4.0    7.0  2  0  0        66.378  33.189  0.3553  4.4652
 1.378   23.0   41.0  1  1  2        67.961  33.981  0.3628  4.5590
 1.358   11.0   20.0  2  0  1        69.098  34.549  0.3681  4.6259
 1.301    2.0    4.0  0  0  4        72.560  36.280  0.3841  4.8268
 1.238    4.0    8.0  2  0  2        76.953  38.476  0.4039  5.0752
 1.181    1.0    2.0  1  0  4        81.368  40.684  0.4231  5.3174
 1.093    7.0   16.0  2  0  3        89.604  44.802  0.4574  5.7479
 1.063    3.0    7.0  2  1  0        92.781  46.390  0.4700  5.9061
 1.042    6.0   14.0  2  1  1        95.301  47.650  0.4797  6.0284
 1.015    4.0   10.0  1  1  4        98.609  49.305  0.4922  6.1845
 0.984    2.0    5.0  2  1  2       102.942  51.471  0.5078  6.3812
 0.976    5.0   13.0  1  0  5       104.130  52.065  0.5120  6.4335
 0.955    1.0    3.0  2  0  4       107.426  53.713  0.5232  6.5751
 0.938    3.0    8.0  3  0  0       110.388  55.194  0.5330  6.6976
 0.906    8.0   22.0  2  1  3       116.274  58.137  0.5513  6.9279
 0.882    4.0   11.0  3  0  2       121.567  60.783  0.5665  7.1193
 0.867    1.0    3.0  0  0  6       125.183  62.591  0.5762  7.2414
 0.837    3.0    9.0  2  0  5       133.925  66.963  0.5973  7.5065
 0.829    1.0    3.0  1  0  6       136.513  68.257  0.6029  7.5767
 0.823    2.0    6.0  2  1  4       138.505  69.253  0.6070  7.6280
 0.812    3.0    9.0  2  2  0       142.910  71.455  0.6154  7.7334
 